Suitability of Anthill Soil as a Supplementary Cementitious Material

##plugins.themes.bootstrap3.article.main##

  •   John Kamau

  •   Ash Ahmed

  •   Paul Hirst

  •   Joseph Kangwa

Abstract

Cement is the most utilised construction material and the second most consumed commodity in the world after water. It has been reported that the heavily energy-intensive processes that are involved in its production contribute about 7 to 10% to the total global anthropogenic carbon dioxide (CO2), which is the main cause of global warming; and are expensive economically. It is however possible, that energy and cost efficiency can be achieved by reducing on the amount of cement, and in its place utilizing Supplementary Cementitious Materials (SCMs), which require less process heating and emit fewer levels of CO2. This work aimed to provide an original contribution to the body of knowledge by investigating the suitability of Anthill Soil (AHS) as an SCM by testing for pozzolanic or hydraulic properties. Cement was replaced in concrete with AHS by weight at 0%, 5%, 7.5%, 10%, 15%, 20%, 25%, and 30% steps at the point of need. The 0% replacement was used as the reference point from which performances were measured. The chemical composition analysis by X-ray diffraction (XRD) showed that AHS contained the required chemical composition for pozzolans, while the compressive strengths achieved were above strength classes that are specified as being suitable for structural applications. The increase in compressive strength over time, density and workability behaviors of AHS were consistent with the characteristics of SCMs. All results across the tests showed good repeatability, highlighting the potential of using AHS as an SCM in concrete to enhance the sustainability and economic aspect of concrete, while at the same time improving its properties in both the wet and hardened states.

Keywords: Anthill Soil, Supplementary Cementitious Materials, Partial Cement Replacements, Pozzolans

References

W. R. Cline, The economics of global warming: The Peterson Institute Press, 1992.

F. Akinboboye, I. Ogunfayo, and H. Dawodu, "Assessment of the Severity of CO2 Emission from Anthill Soils Used as Replacement for Shale in Cement Manufacture," International Journal of Academic Research in Business and Social Sciences, vol. 2, No.12, 2012.

E. J. O'Brien, A. S. Dixon, and E. Sheils, Reinforced and Prestressed Concrete Design to EC2: The Complete Process: Spon Press, 2012.

M. Islam and M. Islam, "Strength and durability characteristics of concrete made with fly-ash blended cement," Australian Journal of Structural Engineering, vol. 14, 2013.

M. E. Johnson and A. Gonzalez, "Estimating Cost Savings for Aviation Fuel and CO 2 Emission Reductions Strategies," Collegiate Aviation Review, vol. 31, 2013.

M. L. Gambhir, Concrete Technology 4e. Tata McGraw-Hill Education, ISBN 0070583749: Tata McGraw-Hill Education, 2009.

K. Quillin, "Calcium Sulfoaluminate Cements—CO2 reduction, concrete properties and applications," BR496, BRE, Garston, UK, 2007.

Mineral Products Association, "Fact Sheet 18 [Part 1] Embodied CO2 of UK Cement," Additions and Cementitious Material, p. 8, 2007.

J. G. Michael, P. Soyka, and D. Conneely, "CO2 Emissions from Cement Production," Good Practice Guidance and Uncertainty Management in National Greenhouse Gas Inventories. Industrial process sector, 2000.

A. Al-Salami and A. Salem, "Effects of mix composition on the sulfate resistance of blended cements," International Journal of Civil & Environmental Engineering, vol. 10, 2010.

K. Sakai and T. Noguchi, The sustainable use of concrete: CRC press, 2012.

B. Lippiatt and S. Ahmad, "Measuring the life-cycle environmental and economic performance of concrete: the BEES approach," in Proceedings of the International Workshop on Sustainable Development and Concrete Technology, 2004, pp. 213-230.

Worldometers. (2016, 09.06.2015). Population. Available: http://www.worldometers.info/world-population/

H. Muga, K. Betz, J. Walker, C. Pranger, A. Vidor, T. Eatmon, et al., "Development of Appropriate and Sustainable Construction Materials," Civil and Environmental Engineering Sustainable Futures Institute, Michigan Technology University, 2005.

K. Steele, G. Cole, G. Parke, B. Clarke, and J. Harding, "The application of life cycle assessment technique in the investigation of brick arch highway bridges," in Proc., Conf. for the Engineering Doctorate in Environmental Technology, 2002.

B. Davison and G. W. Owens, Steel designers' manual: Wiley. com, 2011.

J. D. Bapat, Mineral admixtures in cement and concrete: CRC Press, 2012.

O. Olafusi and F. Olutoge, "Strength properties of corn cob ash concrete," Journal of Emerging Trends in Engineering and Applied Sciences, vol. 3, pp. 297-301, 2012.

F. F. Udoeyo and S. A. Abubakar, "Maize-cob ash as filler in concrete," Journal of materials in civil engineering, vol. 15, pp. 205-208, 2003.

A. Skempton, "The colloidal activity of clays," Selected Papers on Soil Mechanics, pp. 106-118, 1953.

A. S. Nene and Y. D. Parihar. (2016, 29.11.2016). Natural Stabilization of soils with special reference to Entomological Considerations. Available: http://www.slideshare.net/ashoknene/natural-satbilization-of-soils

American Society for Testing and Materials, "ASTM C618. Standard specification for coal fly ash and raw or calcined naturalpozzolan for use in concrete, American Society for Testing and Materials, ASTM International, West Conshohocken, PA, 2012, DOI: 10.1520/C0618-12," ed, 2012.

British Standards Institution, "BS EN 450-1-2012. Fly ash for concrete: Part 1: Definition, specifications and conformity criteria. BSI, London, UK," ed, 2012.

M. Uysal and M. Sumer, "Performance of self-compacting concrete containing different mineral admixtures," Construction and Building materials, vol. 25, pp. 4112-4120, 2011.

C. Arya, Design of structural elements: concrete, steelwork, masonry and timber designs to British standards and Eurocodes. Spon Press, LONDON AND NEW YORK: Taylor & Francis, 2009.

M. Shetty, Concrete technology: theory and practice: S. Chand. ISBN 8121900034, 2005.

British Standards Institution, "BS EN 197-1:2000. Part 1. Cement composition, specifications and conformity criteria for common cements. British Standards Institution (BSI), London, UK," in BSOL, ed, 2000.

British Standards Institution, "BS 3762-4.2:1986 ISO 697:1981. Analysis of formulated detergents —Part 4: Physical test methods —Section 4.2 Method for determination of apparent bulk density. BSI, London, UK," in BSOL, ed, 1999.

R. Grossman and T. Reinsch, "2.1 Bulk density and linear extensibility," Methods of Soil Analysis: Part 4 Physical Methods, pp. 201-228, 2002.

British Standards Institution, "BS EN 12390-1:2012. Testing hardened concrete. Part 1: Shape, dimensions and other requirements for specimens and moulds. BSI, London, UK," ed, 2012.

British Standards Institution, "BS EN 12390-2:2009. Making and curing specimens for strength tests. BSI, London, UK," ed, 2009.

European Ready Mixed Concrete Organisation, "Guidance to the engineering properties of concrete," 2006.

D. Adesanya and A. Raheem, "A study of the permeability and acid attack of corn cob ash blended cements," Construction and Building Materials, vol. 24, pp. 403-409, 2010.

American Society for Testing and Materials, "ASTM C192/C192M. Standard Practice for Making and Curing Concrete Test Specimens in the Laboratory. 16a, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States," ed, 2016.

F. A. Oluokun, "Fly ash concrete mix design and the water-cement ratio law," Materials Journal, vol. 91, pp. 362-371, 1994.

British Standards Institution, "BS 5328: 1990 Part 2: 1990. Concrete. Part 2. Methods for specifying concrete mixes. BSI, London: UK," in BSOL, ed, 1990.

British Standards Institution, "BS 5328: Part 1: 1990. Concrete. Part 1 Guide to specifying concrete. BSI, London: UK," in BSOL, ed, 1990.

American Society for Testing and Materials, "ASTM C1012/C1012M−15. Standard Test Method for Length Change of Hydraulic-Cement Mortars Exposed to a Sulfate Solution1. 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States," ed, 2015.

British Standards Institution, "BS EN 12390-3:2009. Testing of Hardened Concrete, Part 3: Compressive strength of test specimens. BSI, London, UK," ed, 2011.

British Standards Institution, "BS EN 12390-6:2009. Testing hardened concrete Part 6: Tensile splitting strength of test specimens. BSI, London, UK," ed, 2010.

M. Sumer, "Compressive strength and sulfate resistance properties of concretes containing Class F and Class C fly ashes," Construction and Building Materials, vol. 34, pp. 531-536, 2012.

British Standards Institution, "BS 8500-1:2015. Concrete – Complementary British Standard to BS EN 206. Part 1: Method of specifying and guidance for the specifier. BSI, London, UK," ed, 2015.

Downloads

Download data is not yet available.

##plugins.themes.bootstrap3.article.details##

How to Cite
[1]
Kamau, J., Ahmed, A., Hirst, P. and Kangwa, J. 2018. Suitability of Anthill Soil as a Supplementary Cementitious Material. European Journal of Engineering Research and Science. 3, 7 (Jul. 2018), 5-11. DOI:https://doi.org/10.24018/ejers.2018.3.7.785.